BaAn HDPE flexible pipe specially designed to protect power and telecommunication cable. It’s manufactured by modern machine line and HDPE material that complies with the international industrial standards.
|
Table 1: Dimension Specification |
||||||||
|
No./ Stt |
Pipe size |
(D1) Outer diameter (mm) |
(D2) Inner diameter (m) |
(a) Wall thickness (mm) |
(t) Pitch (mm) |
Standard length per coil (m) |
Min. bending radius (mm) |
Standard outer diameter and height of coil (m) |
|
1 |
BFP Ø32/25 |
32 ± 2,0 |
25 ± 2,0 |
1,5 ± 0,30 |
8 ± 0,5 |
200 ÷ 500 |
90 |
1,0 x 0,50 |
|
2 |
BFP Ø40/30 |
40 ± 2,0 |
30 ± 2,0 |
1,5 ± 0,30 |
10 ± 0,5 |
200 ÷ 500 |
100 |
1,2 x 0,50 |
|
3 |
BFP Ø50/40 |
50 ± 2,0 |
40 ± 2,0 |
1,5 ± 0,30 |
13 ± 0,8 |
200 ÷ 500 |
150 |
1,5 x 0,60 |
|
4 |
BFP Ø65/50 |
65 ± 2,5 |
50 ± 2,5 |
1,7 ± 0,30 |
17 ± 1,0 |
100 ÷ 200 |
200 |
1,6 x 0,60 |
|
5 |
BFP Ø85/65 |
85 ± 2,5 |
65 ± 2,5 |
2,0 ± 0,30 |
21 ± 1,0 |
100 ÷ 200 |
250 |
1,7 x 0,65 |
|
6 |
BFP Ø105/80 |
105 ± 3,0 |
80 ± 3,5 |
2,1 ± 0,30 |
25 ± 1,0 |
100 ÷ 200 |
300 |
1,8 x 0,70 |
|
7 |
BFP Ø110/90 |
110 ± 3,5 |
90 ± 3,5 |
2,1 ± 0,35 |
25 ± 1,0 |
100 ÷ 200 |
350 |
1,9 x 0,75 |
|
8 |
BFP Ø130/100 |
130 ± 4,0 |
100 ± 4,0 |
2,2 ± 0,40 |
30 ± 1,0 |
100 ÷ 200 |
400 |
2,0 x 0,85 |
|
9 |
BFP Ø145/115 |
145 ± 4,0 |
115 ± 4,0 |
2,3 ± 0,40 |
34 ± 1,0 |
100 ÷ 200 |
400 |
2,2 x 0,9 |
|
10 |
BFP Ø160/125 |
160 ± 4,0 |
125 ± 4,0 |
2,4 ± 0,40 |
38 ± 1,0 |
50 ÷ 100 |
400 |
2,4 x 1,00 |
|
11 |
BFP Ø195/150 |
195 ± 4,0 |
150 ± 4,0 |
2,8 ± 0,40 |
45 ± 1,5 |
50 ÷ 100 |
500 |
2,5 x 1,20 |
|
12 |
BFP Ø230/175 |
230 ± 4,0 |
175 ± 4,0 |
3,5 ± 1,00 |
55 ± 1,5 |
50 ÷ 100 |
600 |
2,6 x 1,70 |
|
13 |
BFP Ø260/200 |
260 ± 4,0 |
200 ± 4,0 |
4,0 ± 1,50 |
60 ± 1,5 |
50 ÷ 100 |
750 |
2,8 x 1,80 |
|
14 |
BFP Ø320/250* |
320 ± 5,0 |
250 ± 4,0 |
4,5 ± 1,50 |
70 ± 1,5 |
30 ÷ 100 |
850 |
3,2 x 2,10 |
* Produce with order
|
No |
Applied Technology |
Application |
|
1 |
Film |
General and industrial film . Shopping bag . T- shirt bag . Trash can liner . Mulching film |
|
2 |
Blow Molding |
Disinfectant bottles . Tubes for cosmertic .Medium containers.Tool boxes. Bottles for bleaching materrial detergen, industrial chemicals |
|
3 |
Injection molding |
Handling and and stacking crates (palltes, etc), container , toy , caps .Flats yarn . Pond liners , gas, chemical tank containment liners. Automotice fuel tank |
|
4 |
Pipe extrusion |
Pressure pipe ( water supply pipe , gas pipe , sewage pipes ) and fittings. Mullti -wall sewage pipes. Conduits for electrical installations . Corrugates pipe |
Note : Meterial is important factor which hass great influence on quality and price of products
|
Physical Properties |
Testing method |
Testing Conditions |
Units |
Value |
|
Melting Index |
ASTM D 1238 |
190oC/2,16 |
g/10 min |
0,12 ÷ 0,18 |
|
Density |
ASTM D 1505 |
23oC |
g/cm3 |
0,955 ÷ 0,958 |
|
Melting Temperrature |
ASTM D 1238 |
10oC /min |
oC |
132 |
|
Vicat Softening Temperature |
oC |
123 |
||
|
Tensile Strength at Yield |
ASTM D 638 |
50 mm/min |
kgf/cm2 |
270 |
|
Tensile Strength at Break |
ASTM D 638 |
50 mm/min |
kgf/cm2 |
350 |
|
Elongation at Break |
ASTM D 638 |
50 mm/min |
% |
>800 |
|
Flexural Modulus |
ASTM D 790 |
_ |
kgf/cm2 |
13000 |
|
IZOD Impact Strength |
ASTM D 256 |
23oC |
kgcm/cm |
>20 |
|
Hardness in Rockwell Scale |
ASTM D 785 |
55 |
||
|
Environmental cracking resistance |
ASTM D 1693 |
h |
>200 |
|
Table 3: Resistance to chemical |
|||
|
Chemicals |
25 oC |
50 oC |
75 oC |
|
HCl, 30% |
• |
• |
• |
|
H2SO4, 20% |
• |
• |
• |
|
HNO3, 10% |
• |
• |
• |
|
Soda, 20% |
• |
• |
• |
|
Amonia, 10% |
• |
• |
• |
|
Formol, 50% |
• |
• |
- |
|
Acetic Acid, 20% |
• |
• |
• |
|
Insulating Oil |
• |
• |
• |
|
Sea Water |
• |
• |
• |
|
Benzine |
• |
º |
- |
|
Gasoline |
• |
º |
- |
|
Methanol |
• |
• |
- |
Note:
• Entirely inert. Applicable
º Slightly affected. Applicable but with precaution
- Not applicable